We fabricated BSCCO-2212(2212) bulk superconductors by using a casting process and evaluated the superconducting properties. The effects of annealhomogeneous and uniform microstructure improved the critical properties and the microstructures of ingot and annealed rods were different with the size of 2212 rod and tube. The critical current(Ic) of rods increased with increasing annealing time, probably due to increased grain size of 2212. Annealing time of the highest Ic for the smaller rod(diameter of 10 mm) was shorter(150 hr) than that of the larger rod(diameter of 16 mm, 400 hr). This size effect seems to be related to different grain sizes of the intermediate phases such as 2201 and secondary phases in the ingot. In addition, we fabricated 2212 tubes from the rod by removing the center region which contained inhomogeneous microstructures. The Ic of 2212 tube with the outer diameter of 16 mm and the thickness of 2 mm was measured to 844 A, which corresponds to the critical current density of 1017 A/cm2 at 77 K.