The unique features of spark plasma sintering process are the possibilities of a very fast heating

rate and a short holding time to obtain fully dense materials. β-SiC powder with 0, 2, 6, 10 wt% of α-SiC

particles (seeds) and 4 wt% of Al-B-C (sintering aids) were spark plasma sintered at 1700-1850oC for 10

min. The heating rate, applied pressure and sintering atmosphere were kept at 100oC/min, 40 MPa and a

flowing Ar gas (500 CC/min). Microstructural development of SiC as function of seed content and temperature

during spark plasma sintering was investigated quantitatively and statistically using image analysis.

Quantitative image analyses on the sintered SiC ceramics were conducted on the grain size, aspect ratio and

grain size distribution of SiC. The microstructure of SiC sintered up to 1700oC consisted of equiaxed grains.

In contrast, the growth of large elongated SiC grains in small matrix grains was shown in sintered bodies at

1750oC and the plate-like grains interlocking microstructure had been developed by increasing sintering temperature.

The introduction of α-SiC seeds into β-SiC accelerated the grain growth of elongated grains during

sintering, resulting in the plate-like grains interlocking microstructure. In the α-SiC seeds added in β-SiC,

the rate of grain growth decreased with α-SiC seed content, however, bulk density and aspect ratio of grains

in sintered body increased.

권호기사

권호기사 목록 테이블로 기사명, 저자명, 페이지, 원문, 기사목차 순으로 되어있습니다.
기사명 저자명 페이지 원문 목차
Convergent 열처리를 통한 Nd_23_Dy_10_Fe_64_TM₂B₁ 소결자석의 보자력 향상 김훈섭 ;김세훈 ;김진우 ;김영도 pp.1-6

Effect of process-control agents on characteristics of amorphous Al-Y-Ni-Co alloy powder produced by mechanical alloying H. V. Nguyen ;J. C. Kim ;J. S. Kim ;Y. J. Kwon ;Y. S. Kwon pp.7-12

Al-B-C 조제 β-SiC의 스파크 플라즈마 소결에 미치는 α-SiC seed 첨가 영향 :미세 구조 변화 조경식 ;이현권 ;이상우 pp.13-22

수소반응속도 제어에 의한 Nd-Fe-B-Ga-Nb 합금의 미세조직 이방화율 향상에 관한 연구 이상협 ;김동환 ;유지훈 ;이동원 ;김병기 pp.23-28

(A)Study on the behavior of combustion wave propagation and the structure of porous TiNi body during self-propagating high-temperature synthesis process Ji Soon Kim ;Victor E. Gjunter ;Jin Chun Kim ;Young Soon Kwon pp.29-35

Production and properties of amorphous TiCuNi powders by mechanical alloying and spark plasma sintering J. C. Kim ;E. H. Kang ;Y. S. Kwon ;J. S. Kim ;Si-Young Chang pp.36-43

코디어라이트 허니컴 압출용 혼합체의 점성거동에 관한 연구 송용익 ;김형태 ;이진구 ;윤원중 ;류성수 pp.44-51

고압비틀림 성형 공정에 의한 Al 분말의 초미세결정 벌크화 및 특성 평가 주수현 ;윤승채 ;이종수 ;김형섭 pp.52-58

Pechini법에 의한 Y-doped SrTiO₃ 분말의 합성 윤미영 ;송락현 ;신동열 ;황해진 pp.59-64

참고문헌 (44건) : 자료제공( 네이버학술정보 )

참고문헌 목록에 대한 테이블로 번호, 참고문헌, 국회도서관 소장유무로 구성되어 있습니다.
번호 참고문헌 국회도서관 소장유무
1 L. J. Schioler: Am. Ceram. Soc. Bull., 64 (l986) 268. 미소장
2 K. Yamada and M. Mohri: Silicon-Carbide Ceramics,S. Somiya and Y. Inomata (Ed.), Uchida Rokakuho Publishing Ltd., (1988) 9. 미소장
3 M. Srinivasam: Structural Ceramics, J. B. Wachtmann.Jr (Ed.), Academic Press, (1989). 미소장
4 W. L. Vaushn and H. G. Maahs: J. Am. Ceram. Soc.,73 (l990) 1540. 미소장
5 S. Prochazka: Ceramics for High Performance Applications,Burke, Gorum and Katz (Ed.), Brook Hill(1974) 239. 미소장
6 W. Bocker and H. Hausner: Powder Metal. Inter., 10(1976) 87. 미소장
7 D. H. Stutz, S. Prochazka and J. Lorenz: J. Am. Ceram.Soc., 68 (1985) 479. 미소장
8 A. H. Heuer, G. A. Fryburg, L. U. Ogbuji and T. E.Mitchell: J. Am. Ceram. Soc., 61 (1978) 406. 미소장
9 L. U. Ogbuji, T. E. Mitchell and A. H. Heuer: J. Am.Ceram. Soc., 64 (1981) 91. 미소장
10 M. Omori and H. Takei: J. Am. Ceram. Soc., 65(1982) C92. 미소장
11 M. A. Mulla and V. D. Kristic: Acta Metall. Mater., 42(1994) 303. 미소장
12 M. A. Mulla and V. D. Kristic: Am. Ceram. Soc. Bull.,70 (1991) 439. 미소장
13 N. P. Padture: J. Am. Ceram. Soc., 77 (1994) 519. 미소장
14 S. H. Kim, Y.-W. Kim and M. Mitomo: J. Mater. Sci.,38 (2003) 1117. 미소장
15 N. P. Padture and B. R. Lawn: J. Am. Ceram. Soc., 77(1994) 2518. 미소장
16 Y. W. Kim, K. S. Cho and J. G. Lee: Kor. J. Ceram., 2(1996) 39. 미소장
17 Y. W. Kim, M. Mitomo and H. Hirotsuru: J. Am.Ceram. Soc., 80 (1997) 99. 미소장
18 R. M. Williams, B. N. Juterbock, S. S. Shinozaki, C.R. Peters and T.J. Whalen: Am. Ceram. Soc. Bull., 64(1985) 1385. 미소장
19 B.-W. Lin, M. Imai, T. Yano and T. Iseki: J. Am.Ceram. Soc., 69 (1986) C67. 미소장
20 S. Shinozaki, R. M. Williams, B. N. Juterbock, W. T.Donlon, J. Hangas and C. R. Peters: J. Am. Ceram.Soc., 64 (l985) l389. 미소장
21 J. J. Cao, W. J. Moherlychan, L. C. De Jonghe, C. J.Gilbert and R. O. Ritchie: J. Am. Ceram. Soc., 79(1996) 461. 미소장
22 W. J. Moberlychan, J. J. Cao and L. C. De Jonghe:Acta Mater., 46 (1998) 1625. 미소장
23 W. J. Moberlychan and L. C. De Jonghe: Acta Mater.,46 (1998) 2471. 미소장
24 D. Chen, M. E. Sixta, X. F. Zhang, L. C. De Jonghe and R. O. Ritchie: Acta Mater., 48 (2000) 4599. 미소장
25 X. F. Zhang, Q. Yang and L. C. De Jonghe: Acta Mater., 51 (2003) 3849. 미소장
26 X. F. Zhang, G. Y. Lee, D. Chen, R. O. Ritchie and L.C. De Jonghe: J. Am. Ceram. Soc., 86 (2003) 1370. 미소장
27 M. Tokita: J. Soc. Powder Technol. Jpn., 30 (1993)790. 미소장
28 N. Tamari, T. Tanaka, K. Tanaka, I. Kondoh, M. Kawahara and M. Tokita: J. Ceram. Soc. Jpn., 103 (1995)740. 미소장
29 T. Nishimura, M. Mitomo, H. Hirotsuru and M.Kawakara: J. Mater. Sci. Lett., 14 (1995) 1046. 미소장
30 D. S. Perera, M. Tokita and S. Moricca: J. Euro.Ceram. Soc., 18 (1998) 401. 미소장
31 Y. Zhou, K. Hirao, M. Toriyama and H. Tanaka: J.Mater. Res., 14 (1999) 3363. 미소장
32 S. W. Wang, L. D. Chen and T. Hirai: J. Mater. Res.,15 (2000) 982. 미소장
33 Y. Zhou, K. Hirao, M. Toriyama and H. Tanaka: J.Am. Ceram. Soc., 83 (2000) 654. 미소장
34 K.-S. Cho, S. Kim, H.-J. Choi, J.-G. Lee and Y.-W.Kim: J. Kor. Ceram. Soc., 38 (2001) 687. 미소장
35 L. Gao, H. Wang, H. Kawaoka, T. Sekino and K. Niihara:J. Euro. Ceram. Soc., 22 (2002) 785. 미소장
36 K.-S. Cho, K.-S. Lee, J.-H. Song, J.-Y. Kim and K.-H.Song: J. Kor. Ceram. Soc., 40 (2003) 751. 미소장
37 W. Chen, U. Anselmi-Tamburini, J. E. Garay, J. R.Graza and Z. A. Munir: Mater. Sci. & Engineer., A394(2005) 132. 미소장
38 U. Anselmi-Tamburini, S. Gennari and Z. A. Munir:Mater. Sci. & Eng., A394 (2005) 139. 미소장
39 K.-S. Cho and K.-S. Lee: Key Eng. Mater., 287 (2005)335. 미소장
40 K.-S. Cho, K.-S. Lee, H.-K. Lee, S. J. Lee and H.-J.Choi: J. Kor. Ceram. Soc., 42 (2005) 567. 미소장
41 K.-S. Cho, Z. A. Munir and H.-K. Lee: J. Ceram. Pro.Res., 9 (2008) 500. 미소장
42 Y.-W. Kim, M. Mitomo and G.-D. Zhan: J. Mater.Res., 14 (1999) 4291. 미소장
43 K. Vanmeensel, A. Laptev, J. Hennicke, J. Vleugels,O. Van der Biest: Acta Mater., 53 (2005) 4379. 미소장
44 Y.-W. Kim, S.-G. Lee and M. Mitomo: J. Euro. Ceram.Soc., 22 (2002) 1031. 미소장

추천서가 (다양한 추천 자료를 만나보세요)

권호기사보기

권호기사 목록 테이블로 기사명, 저자명, 페이지, 원문, 기사목차 순으로 되어있습니다.
기사명 저자명 페이지 원문 기사목차

권호

기사명 원문보기 기사목차
닫기